Alloy Steel A333 Gr. 6 Seamless Pipe

• Customization: Available
• Type: Pipe
• Standard: AISI, ASTM, DIN, GB, BS
• Model NO.: 1/2" TO 24"
• Technique: Cold Drawn
• Shape: Round
• Surface Treatment: Color Coated
• Special Use: High-strength Steel Plate
• Application: Cold Area
• Steel Grade: Gr6
• Transport Package: as Clients Requirments
• Specification: 1/2" TO 24"
• Trademark: DATANG
• Origin: China
• Production Capacity: 50000 Per Year

Product Description

Alloy steel pipes have low temperature type and boiler alloy pipes.  A333 GR6 STEEL PIPE is normally use alloy pipes in cold place.In order to provide One-Stop service for customers with superior products from qualified supplier.
Material for alloy we have  T1,T2,T5,T9,T11,T12,T22,T91,T92,P1,P2,P5,P9,P11,P12,P22,P91,P92,15CrMO,Cr5Mo,10CrMo910,12CrMo,
13CrMo44,30CrMo,A333 GR.1,GR.3,GR.6,GR.7,etc
Thickness    2-80mm
Outer Diameter    21.3-610mm
Length    Fixed or Random ,by customer's requiremnts
Country of origin    China
Productivity    50000 Metric Tons pet year
Application:    Scaffolding pipe, Structure pipe,
Lowpressure fluid pipe for water oil or gas pipe.
 

izes Range
OD:19.05mm-457mm, WT:2.0mm-60mm
Length: Lengths required shall be specified on order.If no definite lengths required, following practice applies: Single Random - 17′ ~ 24′ lengths Double Random - 36′ ~ 44′ lengths

 

Heat Treatment Requirements:

All seamless and welded pipe shall be treated to control their microstructure by the following methods:

Normalizing per ASTM A333 Standard Specification for Seamless and Welded Steel Pipe 

 

Quenched and Tempered per A 333/A 333M - 05

 

Testing:

Inspection and Test: Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength,Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test,No-destructive Test, Hydrostatic Test.

For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot.

For small lots, at least one pipe shall be tested.

For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.

Hydrostatic Test

Impact Test One notched bar impact test, consisting of breaking three specimens shall be made from each heat represtented in a heat-treatment load on specimens taken from the finished pipe.