ASTM A333 Gr6 Low Temperature Steel Pipe/Tube

• Type: Pipe
• Standard: AISI, ASTM, DIN, GB, BS
• Composition: Alloy Steel
• Technique: Cold Drawn
• Shape: Round
• Surface Treatment: Color Coated
• Model NO.: Outer Diameter: 1/8"-36"(10.3mm-914.4mm)
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel, Cold Environment
• Application: Cold Area
• Steel Grade: Gr6
• Sample: Avaliable
• Advantage: Rich Experience
• Packing: Wooden Box
• MOQ: 1 Piece
• Feature: Corrosion Resistance
• Transport Package: as Clients Requirments
• Specification: 1/2" TO 24"
• Trademark: DATANG
• Origin: China
• HS Code: 7304192000
• Production Capacity: 50000 Per Year

Product Description

Standard: ASTM A213, A333, A335
Steel Grade:T2-T22 Gr1 to Gr9 P1to P91 etc
Size and OD: 1/8"-24"(10.3mm-610mm)
Wall Thickness: SCH10... STD,SCH40,SCH80...SCH160,XS,XXS.



 

Standard	Steel Grade	Chemical Components							Machanical Property
		C	Mn	Si	Cr	Mo	P	S	Tensile Strength (Mpa)	Yield Strength(Mpa)
ASTM A333	Gr6	≤0.30	0.29~1.06	≥0.10			≤0.025	≤0.025	≥415	≥240
ASTM A335	P1	0.10-0.20	0.30-0.80	0.10-0.50		0.44~0.65	≤0.025	≤0.025	≥380	≥205
	P5	≤0.15	0.30~0.60	≤0.50	4.00~6.00	0.45~0.65	≤0.025	≤0.025	≥415	≥205
	P9	≤0.15	0.30~0.60	0.25~1.00	8.00~10.00	0.90~1.10	≤0.025	≤0.025	≥415	≥205
	P11	0.05~0.15	0.30~0.60	0.50~1.00	1.00~1.50	0.44~0.65	≤0.025	≤0.025	≥415	≥205
	P12	0.05~0.15	0.30~0.61	≤0.50	0.80~1.25	0.44~0.65	≤0.025	≤0.025	≥415	≥220
	P22	0.05~0.15	0.30~0.60	≤0.50	1.90~2.60	0.87~1.13	≤0.025	≤0.025	≥415	≥205

The process begins with solid steel rounds, or billets, being cut to a specified length and sent through a walking-beam reheat furnace, where temperatures reach nearly 2,300°F.

After exiting the reheat furnace, the preheated rounds are turned into a tube shell in the rotary piercing mill as the billets are cross-rolled between two barrel-shaped rolls at a high speed.

The seamless shells enter mandrel mill, where they are rolled over a retained mandrel to provide the needed OD size and wall thickness for the next process. The process is carefully monitored using a state-of-the-art hot-wall measuring system.

The shells are then reheated for final forming in a 24-stand stretch-reducing mill, where outside diameters are formed to customers' exacting specifications. Wall thickness is again verified using a hot-wall measuring system.

After being rotated and advanced on the walking-beam cooling bed, the pipes are batch cut and transferred to an in-process storage area, where they are handled by computer-controlled gantry cranes.